Design and Preparation of Nanoporous Cu/Ag Multilayer Films
点击次数：
DOI码：10.3390/coatings11101187
发表刊物：Coatings
关键字：nanoporous films; multilayer; magnetron sputtering; dealloying; nanoporous multilayer
摘要：Cu30Al70 and Ag30Al70 multilayer precursor films were prepared by magnetron sputtering, respectively. Then the nanoporous Cu/Ag multilayer composite films were successfully prepared by selecting the appropriate H2SO4 solution as the dealloying solution. It was found that the nanoporous structure was stable in the dealloying solution. The morphology and structure of nanoporous multilayer films are mainly related to the phase composition of precursors. The structure of nanoporous multilayers can be simply regarded as the superposition of single-layer structures. Our work shows that nanoporous multilayers can be well-prepared by magnetron sputtering combined with dealloying.
第一作者：Yufei Wang
论文类型：期刊论文
通讯作者：Engang Fu,Jing Wang,Zhaoyi Hu
论文编号：1187
学科门类：工学
期号：11
是否译文：否
发表时间：2021-09-29
收录刊物：SCI
上一条： Significant suppression of void swelling and irradiation hardening in a nanograined/nanoprecipitated 14YWT-ODS steel irradiated by helium ions, Journal of Nuclear Materials
下一条： Wang, Jing; Hatano, Yuji*; Hinoki, Tatsuya; Alimov, Vladimir Kh.; Spitsyn, Alexander V.; Bobyr, Nikolay P.; Kondo, Sosuke; Toyama, Takeshi; Lee, Heun Tae; Ueda, Yoshio; Schwarz-Selinger, Thomas; Deuterium retention in W and binary W alloys irradiated with high energy Fe ions, Journal of Nuclear Materials, 2021, 545(1): 0-152749.