Investigation of the Y Effect on the Microstructure Response and Radiation Hardening of PM V-4Cr-4Ti Alloys after Irradiation with D Ions
发布时间：2023-10-19点击次数：
- DOI码：10.3390/met13030541
- 发表刊物：Metals
- 关键字：ion irradiation; vanadium alloy; powder metallurgy; yttrium; segregation
- 摘要：In the current work, an analysis of the effects of Y on the radiation hardening and microstructure response of a V-4Cr-4Ti alloy has been conducted after 30 keV D ion irradiation at room temperature using transmission electron microscopy (TEM) and nanoindentation. The results show that the formation of large Y2O3 and small Y2V2O7 nanoparticles was confirmed, indicating that the addition of Y reduces the amount of dissolved oxygen. The addition of Y has been shown to affect the radiation-induced dislocation loops, radiation hardening, and Ti-rich segregation of the V-4Cr-4Ti alloy. With the addition of Y, the mean size of the radiation-induced dislocation loop decreased, which may result from the strong sink strength of the nanoparticle/matrix interface, interactions between Y atoms and SIA clusters, and the strong binding energy of vacancy–oxygen pairs. Some particles with core–shell structures were observed after ion irradiation, where Ti-rich segregations at the nanoparticle/matrix interface were confirmed. These results indicate that Y might promote abnormal segregation. Possible causes for this include the lower interface energy at the particle/matrix interface and the interaction between oxygen and solute atoms.
- 第一作者：Yifan Zhang
- 论文类型：期刊论文
- 通讯作者：Jing Wang
- 论文编号：541
- 学科门类：工学
- 期号：13
- 是否译文：否
- 发表时间：2023-03-08
- 收录刊物：SCI